Abstract
The behavior of reinforced concrete beams containing fibers made of waste plastic straws (WPSs) under the three point bending test is examined. The e ect of WPS fiber addition on the compressive and split tensile strength is reported. Four concrete mixes were prepared. The control mix PS-0 had a proportion of 1 cement: 1 sand: 2 coarse aggregate and a water cement ratio of 0.4. In the other three mixes PS-0.5, PS-1.5 and PS-3, 0%, 0.5%, 1.5% and 3% of WPS fiber (by volume) was added respectively. The results show that at 0.5% WPS, there is slight increase in compressive strength. However, beyond 0.5% addition, a decrease in compressive strength is observed. The split tensile strength shows a systematic increase with the addition of WPS fibers. The reinforced concrete beams containing WPS fibers show higher ductility as demonstrated by the larger ultimate tensile strain and ductility index (Du/Dy). There is a tendency to have more fine cracks with the presence of WPS fibers. arabic 9 English 76